1.Excellent Thermal Shock Stability
2.Excellent Corrosion Resistance Performance
Mainly used in refining furnace such as AOD, VOD, RH, DH, SKF, etc.
Contact us
Liuzhai Town, Xinmi City, Henan, China, 452370
Description of Salt-Impregnated Magnesia Chrome Brick
Salt-Impregnated Magnesia Chrome Brick is made of fused MgO-Cr2O3 grains, high-purity fused or sintered magnesia and chrome concentrate at high temperature.
Salt-Impregnated Magnesia Chrome Brick is characterized by thermal shock resistance of direct bonded magnesia-chromite bricks and corrosion resistance performance of fused rebonded magnesia-chromite bricks. Mainly used in refining furnace such as AOD, VOD, RH, DH, SKF, etc.
Technical Dates of Salt-Impregnated Magnesia Chrome Brick
Item Brand | MgO (%)≥ | Cr2O3 (%)≥ | SiO2 (%)≤ | A. P. (%)≤ | C.C.S. (MPa)≥ | R.U.L@0.2MPa &T0.6(℃)≥ | Thermal Expan. (1400℃ ) % |
HXMSRMGe-12A | 78 | 12 | 1.5 | 15 | 45 | 1700 | 1.4 |
HXMSRMGe-12B | 75 | 12 | 2.0 | 16 | 40 | 1700 | / |
HXMSRMGe-14A | 75 | 14 | 1.5 | 15 | 45 | 1700 | / |
HXMSRMGe-14B | 72 | 14 | 2.0 | 16 | 40 | 1700 | / |
HXMSRMGe-16A | 72 | 16 | 1.5 | 15 | 45 | 1700 | 1.5 |
HXMSRMGe-16B | 70 | 16 | 1.8 | 16 | 40 | 1700 | / |
HXMSRMGe-18A | 70 | 18 | 1.5 | 15 | 45 | 1700 | / |
HXMSRMGe-18B | 68 | 18 | 2.0 | 16 | 40 | 1700 | / |
HXMSRMGe-20A | 68 | 20 | 1.5 | 15 | 45 | 1700 | 1.6 |
HXMSRMGe-20B | 65 | 20 | 2.0 | 16 | 40 | 1700 | / |
HXMSRMGe-22 | 65 | 22 | 2.0 | 16 | 45 | 1700 | / |
HXMSRMGe-26 | 60 | 26 | 2.0 | 16 | 45 | 1700 | 1.7 |
HXMSRMGe-30 | 55 | 30 | 2.0 | 16 | 45 | 1700 | / |