FA-80 Steel Fiber Reinforced Refractory Castable
Made of the super high grade bauxite clinker as main grain, the good quality bauxite clinker and corundum powder as substrate, super fine powder etc. Composite as bonding agent or adding agent, also adding the heating resistance stainless steel fiber.
Steel Fiber Castable Feature
High strength, high wearing-resisting, strong thermal shock stability, etc. Features.
Steel Fiber Castable Application
Mainly used in the front entrance (kiln-head cover) zone of the cement rotary kiln of above new type of dry method 2500 TPD cement plant, also used in the cooler, coal burner, precalciner, preheater, etc. Zones of the cement kiln.
Contact us
Liuzhai Town, Xinmi City, Henan, China, 452370
FA-80 Steel Fiber Reinforced Refractory Castable
Made of the super high grade bauxite clinker as main grain, the good quality bauxite clinker and corundum powder as substrate, super fine powder etc. Composite as bonding agent or adding agent, also adding the heating resistance stainless steel fiber.
Steel Fiber Castable Feature
High strength, high wearing-resisting, strong thermal shock stability, etc. Features.
Steel Fiber Castable Application
Mainly used in the front entrance (kiln-head cover) zone of the cement rotary kiln of above new type of dry method 2500 TPD cement plant, also used in the cooler, coal burner, precalciner, preheater, etc. Zones of the cement kiln.
Technical Dates of Steel Fiber Castable
ITEM
PROPERTY | Hi-Al2O3 Castable
HXPA-801 | Steel Fiber Reinforced Refractory Castable HXPA-802 | High Strength High Al2O3 Castable HXPA-803 | |
Al2O3+SiC % ≥ | 75 | 75 | 80 | |
SiO2 % ≤ | 20 | 20 | 18 | |
Max working Temp.(℃) | 1500 | 1600 | 1600 | |
B. D. g/cm3 ≥ | 2.50 | 2.55 | 2.60 | |
C. C. S. (MPa)≥ | 110℃×24h | 40 | 50 | 60 |
1100℃×3h | 35 | 40 | 50 | |
M.O.R (MPa)≥ | 110℃×24h | 4.0 | 4.0 | 5.0 |
1100℃×3h | 5.0 | 6.0 | 7.0 | |
P.L.C (%) | 1100℃×3h | -0.1-----0.5 | -0.1-----0.5 | -0.1-----0.3 |
Adhesive Solution Adding rate % | 18 | 16 | 16 | |
Method of installation | Vibration style |
*They are typical values in this table, not a basis for order.